Abstract

Objective: To evaluate the effects of tooth whitening with 10% carbamide peroxide on the surface ultramorphology of three dental restorative materials. Materials and methods: Three materials were tested: (1) a reinforced zinc oxide-eugenol cement (IRMR Powder Zinc Oxide Eugenol, Dentsply, Konstanz, Germany), (2) a high copper amalgam with spherical particles (Ventura FinestR, Madespa SA, Toledo, Spain) and (3) a nanohybrid composite (EvoCeram TetricR, Ivoclar Vivadent AG, Schaan, Liechtenstein). 6 specimens of each material (N= 18) were inserted into silicone molds with circular cavities of 10mm×2mm. 3 specimens of each material were randomly assigned into the whitening or control groups. In the whitening group, the specimens were exposed to a 10% carbamide peroxide gel (OpalescenceR PF 10%, Ultradent, South Jordan, UT, USA) for 14 consecutive days, 6h per day. In the control group, the specimens were exposed to distilled water. After 14 days stored at 37 °C, all specimens were analyzed by scanning electron microscopy. Results: The specimens exposed to carbamide peroxide revealed an irregular surface, with cracks and pores. Specimens from all control groups showed a smooth surface. Conclusion: The 10% carbamide peroxide gelmay cause changes in surface ultramorphology of the materials tested: reinforced zinc oxide-eugenol cement, amalgam and composite. c 2011 Sociedade Portuguesa de Estomatologia e Medicina Dentaria. Published by Elsevier Espana, S.L. All rights reserved.

Resumo

Objectivos: Avaliar os efeitos do branqueamento dentário com peróxido de carbamida a 10% na ultra-morfologia de superfície de materiais restauradores dentários. Materiais e Métodos: Foram testados três materiais: 1) um cimento de óxido de zinco-eugenol reforçado (IRMR Powder Zinc Oxide Eugenol, Dentsply, Konstanz, Alemanha), 2) um amalgama de alto teor de cobre de partículas esféricas (Ventura FinestR, Madespa SA, Toledo, Espanha) e 3) um compósito nanohíbrido (Tetric EvoCeramR, Ivoclar Vivadent AG, Schaan, Liechtenstein). 6 especimes de cada material (N = 18) foram inseridos em moldes de silicone com cavidades circulares de 10mm x 2mm. 3 especimes de cada material foram distribuídos aleatoriamente para os grupos de branqueamento ou de controlo. No grupo de branqueamento, os especimes foram expostos a um gel de peróxido de carbamida a 10% (Opalescence PF 10%R, Ultradent, South Jordan, UT, EUA) durante 14 dias seguidos, 6 horas diárias. No grupo de controlo, os especimes foram expostos a água destilada. Após 14 dias de armazenamento a 37 °C, todos os especimes foram analisados através de microscopia eletrónica de varrimento. Resultados: Os especimes expostos ao peróxido de carbamida revelaram uma superfície irregular, com fendas e poros. Os dos grupos de controlo apresentaram uma superfície regular. Conclusão: O gel de peroxido de carbamida a 10% pode causar alterações na ultra-morfologia de superfície dos materiais testados: cimento de oxido de zinco-eugenol reforçado, amalgama e compósito. c 2011 Sociedade Portuguesa de Estomatologia e Medicina Dentária. Publicado por Elsevier Espana, S.L. Todos os direitos reservados.